Model No.: 60 Series F603200C-100Ah
Hayat perkhidmatan yang panjang 60 Series Cylindrica lifepo4 F603200C-100Ah bateri untuk power bank bank
Persembahan Bas ic
No. |
Item |
Specification |
1 |
Nominal Capacity |
100Ah ,0.5 C discharging(25±2℃) |
2 |
Nominal Voltage |
3.2V |
3 |
Charge Ending Voltage |
3.65V |
4 |
Discharge Ending Voltage |
2.5V(≥0℃) 2.0V(< 0℃) |
5 |
Standard Charging Method |
25±2℃ 0.5C constant current charge to 3.65V, then constant voltage 3.65V charge till charged current declines to ≤ 0.05C |
6 |
Standard Discharging Method |
25±2℃ 0.5C constant current discharge to 2.5V |
7 |
Max.Pulse Charging Current |
1.5C (15℃~45℃, 50%SOC) ≤30S |
8 |
Max.Pulse Discharging Current |
2C (15℃~45℃, 50%SOC) ≤30S |
9 |
Operating environment |
Charging: -0℃-55℃, max.90%RH Discharging: -20℃-55℃, max.90%RH |
10 |
Impedance |
<0.6mΩ |
11 |
Cell Weight |
1.90kg±0.20kg
|
12 |
Mass Energy Density |
168Wh/Kg
|
13 |
Volume Energy Density |
364Wh/L
|
Ciri Elektrik
NO. |
Item |
Criterion |
Test Method |
1 |
0.5C discharging capacity |
Discharging capacity is not less than normal capacity. |
After Standard Charging, rest 5 minutes ,then 0.5C discharge to ending voltage. |
2 |
Room temperature 1C discharging capacity(initial capacity) |
Discharging capacity must be not less than nominal capacity and no more than 110% nominal capacity. Range:≤5% the average of initial capacity |
After the cell is charged with 1C,and then discharge it to 2.5V with 1C.Repeat 5 times(If the range of capacity is no more than 3% nominal capacity and sustains 3 times,stop the test early),average the last three. 1C |
3 |
Standard cycle life
|
Discharging capacity is not less than 80% initial capacity when have cycled 2000 times |
Test condition: 25±2℃ Charge:1C to 3.65V, then constant voltage 3.65V charge till charged current declines to ≤ 0D.i0s5cCharge:1C to 2.5V When the discharge capacity reduced to 80% of rated capacity, Stop testing |
4 |
Ratio discharging capacity |
Discharging capacity should be not less than 90% initial capacity |
After the cell is charged with 1C,and then discharge it to 2.5V with 3C.Compare with the initial capacity. |
5 |
Ratio charging performance |
Discharging capacity should be not less than 80% initial capacity |
After the cell is charged with 2C,and then discharge it to 2.5V with 1C。Compare with the initial capacity. |
6 |
Low temperature discharging capacity |
Discharging capacity should be not less than 70% initial capacity |
After the cell is charged with 1C,keep the cell at -20℃±2℃ for 24 hours,and then discharge it to 2.0V with 1C at -20℃±2℃。Compare with the initial capacity. |
7 |
High temperature discharging capacity |
Discharging capacity should be not less than 90% initial capacity |
After the cell is charged with 1C,keep the cell at 55℃±2℃ for 5 hours,and then discharge it to 2.5V with 1C at 55℃±2℃。Compare with the initial capacity. |
8 |
Charge retention capacity and recovering capacity of room temperature |
Charge retention capacity should be not less than 85% initial capacity ; recovering capacity should be not less than 90% initial capacity |
After the cell is charged with 1C,keep the cell at room temperature for 28days , and then discharge it to 2.5V with 1C at room temperature. Metering the charge retention capacity;Then the battery should be charged with 1C and should be discharged with 1C at room temperature. Metering the recovering capacity. |
9 |
Charge retention capacity and recovering capacity of high temperature |
Charge retention capacity should be not less than 85% initial capacity ; recovering capacity should be not less than 90% initial capacity |
After the cell is charged with 1C,keep the cell at 55℃±2℃ for 7daysand rest 5h at room temperature,discharge it to 2.5V with 1C at room temperature. Metering the charge retention capacity ; Then the cell should be charged with 1C and should be discharged to 2.5V with 1C at room temperature. Metering the recovering capacity. |
10 |
Appearance |
The surface of cell should be dry and labeled clearly,and without burr , scratch , contamination,distortion, break and so on |
Visual inspection |
11 |
Polarity |
The cell polarity should be labeled clearly and correctly |
Measured with voltmeter |
12 |
Dimension and Weight |
The cell dimension and weight accord with stated value |
Using measuring tools and electronic scale |
13 |
Storage |
Discharging capacity should be not less than 90% initial capacity |
After the cell is charged with 1C,and then discharge it with 1C in 30min at room temperature. Keep the cell at 45℃±2℃for 28days and rest 5h at room temperature. Then the cell should be charged with 1C and should be discharged to 2.5V with 1C at room temperature. Metering the discharging capacity. |
Ciri Persekitaran
NO |
Item |
Criterion |
Test Method |
1 |
Constant temperature and constant humidity test |
No explosion,no fire, no leakage. Discharging capacity is not less than 85% initial capacity |
After Standard Charging, test condition: Temperature:40±5℃ Relative Humidity:90~95%RH Storage Time:48 hours Then return to room temperature for 2 hours, Then 0.5C discharged to ending voltage. |
2 |
Vibration test |
No explosion, no fire,no Leakage |
After Standard Charging , fixed the cell to vibration table, then subjected to vibration testfor 30 minutes per axis of XYZ axes. Frequency rate:1oct/min Vibration frequency:10Hz-30Hz Excursion (single amplitude):0.38mm Vibration frequency:30Hz-55Hz Excursion (single amplitude):0.19mm |
3 |
Shock test |
No explosion, no fire,no leakage |
After Standard Charging,test condition: Acceleration:100m/s2 Pulse lasting time:<16ms Shock times:1000±10 times |
Ciri-ciri Keselamatan
1 |
Overcharge test |
No explosion,no fire |
After the cell is charged with 1C , test condition: Charge : 1C to 5.475V When the voltage get to 5.475V or charge for 60 min ,Stop testing and observe 1h.
|
2 |
Over-discharge test |
No explosion,no fire,no leakage |
After the cell is charged with 1C,discharge 90 min at 1C,stop testing and observe 1 h. |
3 |
Short-circuit test |
No explosion, no fire |
After the cell is charged with 1C,Short circuit the positive and negative 10 min,and the resistance of the external line is not more than 5mΩ,Stop testing and observe 1h. |
4 |
Free fall test |
No explosion,no fire,no leakage |
After the cell is charged with 1C,the positive and negative terminal face down,and then cell falls freely from the height of 1.5m down to the cement floor,and observe 1h. |
5 |
Heating test |
No explosion, no fire |
After the cell is charged with 1C,Put cell into a hot box. Test condition: Temperature rate :5℃ /min Ending temperature :130℃±2℃ Keep temperature for 30 minutes ,then stop testing and observe 1 h. |
6 |
Crush test |
No explosion, no fire |
After the cell is charged with 1C,fixing the cell. Test condition: Direction of extrusion:perpendicular to the pole piece Crushing speed:(5±1)mm/s Crushing plate:A half cylinder with a radius of 75mm,longer than the cell When the voltage reach 0V or eformation get to 30% or extrusion force get to 200kN,stop testing and observe 1 h. |
7 |
Seawater immersion test |
No explosion, no fire |
After the cell is charged with 1C,put the cell into seawater or saltwater. Test condition: Concentration:3.5% NaCl After 2 h,stop testing and observe 1 h. |
8 |
Temperature cycling test |
No explosion,no fire,no leakage |
After the cell is charged with 1C,put the cell into a High-low Temperature Chamber. Test condition: First stage : decrease the temperature from 25℃ to -40℃ Decrease temperature time:60min Holding time:90min Second stage : raise the temperature from -40℃ to 25℃ Raise temperature time:60min Third stage:raise the emperature from 25℃ to 85℃ Raise temperature time:90min Holding time:110min Forth stage : decrease the temperature from 85℃ to 25 Decrease time:70 min Change the temperature from the first stage to the forth stage and cycle five times,then stop testing and observe 1 h. |
9 |
Low pressure test |
No explosion,no fire,no leakage |
After the cell is charged with 1C,put the cell into a Vacuum Chamber. Test condition: Pressure:11.6 kPa Temperature:room temperature Time:6h then stop testing and observe 1 h. |
Note: Above testing of safe characteristics must be with protective equipment. |
Huachuang Times adalah syarikat teknologi bateri canggih di China, yang memfokuskan pada R&D dan produksi dalam bidang bateri kecil, berkeras untuk menjadikan sains dan teknologi sebagai pendahulu, memfokuskan pada produk dan memberi tumpuan kepada pelanggan.
Syarikat ini telah menubuhkan pusat teknologi dan stesen penyelidikan ilmiah pasca-doktoral, dan telah menubuhkan sejumlah pusat penyelidikan tenaga baru dengan kerjasama universiti-universiti utama nasional dan Institut Akademi Sains Cina. Mekanisme penyelidikan dan inovasi saintifik sudah matang dan lengkap. Sebagai sebuah syarikat yang mempunyai kekuatan saintifik dan teknologi yang kuat dalam bidang bateri di China, ia akan memberikan komitmen kepada Pengguna untuk menyediakan produk dan perkhidmatan tenaga dengan teknologi dan pengalaman baru.
Hari ini, produk syarikat telah dijual ke lebih dari 60 negara dan wilayah di lima benua di dunia, menunjukkan kualiti produk Cina yang sangat baik dan daya tarikan perusahaan nasional yang kuat kepada pengguna.
Kategori produk : Pek Bateri Litium Polimer > 60 Siri Bateri Lithium-ion Silinder LFP
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.